Main use:
Used in metal, copper, ceramics, circuit boards, glass fiber, ABS, PVC, electrical and electronic parts insulators, shockproof, and then fixed, suitable for power, speakers, toys, speakers, furniture, electrical appliances, handbags and other industries.
Technical characteristics:
|
|
Performance
|
UL-1608
|
MX-508
|
SC-608
|
|
3
|
main ingredient
|
Neoprene/polyurethane
|
Polyester resin
|
Polyester resin
|
|
4
|
Exterior
|
Light yellow liquid
|
White
|
White
|
|
5
|
Viscosity (25"C/CPS)
|
80000±1000
|
40000~60000
|
60000~100000
|
|
6
|
Curing point (%)
|
62±2%
|
62+2%
|
62+2%
|
|
7
|
Specific gravity
|
1.30±0.05
|
1.30±0.05
|
1.0±0.05
|
|
9
|
Dry time (minutes)
|
2~5
|
2~4
|
2~4
|
|
10
|
Saveable time (25"C)
|
6 months
|
6 months
|
6 months
|
|
11
|
Flame resistance point
|
260 ° C
|
260 ° C
|
200 ° C
|
|
12
|
temperature resistance
|
-30~140°C
|
-30~140°C
|
-30~140°C
|
|
13
|
Packing
|
18KG/3KG
|
18KG/3KG
|
18KG/3KG/180ML
|
Instructions for use:
1. Moisture, dust, oil, etc. on the surface of the material to be subsequently removed must be removed first.
2. Coating method: The tool such as a brush is evenly coated with the adhesive on both sides of the material to be coated, and the coating amount is 150-250 g/m3.
3. After the application, the material is applied at room temperature for 2 to 5 minutes, and then adhered to the line.
4, forced drying: 50 ~ 60 ° C for about 4 to 6 minutes, 80 ° C for about 2 to 3 minutes.
5. This adhesive is a solvent-based adhesive, which is flammable before drying. Therefore, it is absolutely prohibited to use fire gas around the operation.