Main use:
This series is a non-solvent type single-copy ring resin product, which is synthesized from no material, has low linear expansion coefficient and high/shenzhen, vibration, and hard clothing. It is widely used in the fixed connection of electronic components, handicrafts and gifts. It has excellent bonding strength for packaging and bonding between metal, porcelain, glass, fiber products and hard plastic: it is recommended for the inductance line diagram. The pressed iron core or the core of the core is fixed. Especially after immersion in tin and solder, it does not affect the strength of the operation.
Technical characteristics:

Serial number	Performance	WL7603	dark grey	dark grey
3	Exterior	Black, gray, white	1500~4500 <100	1.4~1.5
4	Specific gravity (25"C)	1.2~1.5	1.3~1.5	1000~3000
5	Viscosity (25"C/CPS)	38000~40000	38000~40000	25000~45000
6	Curing time (100‘c/120"c)	1.5h/1h	1.5h/1h	2.5h/1.5h
7	Hardness (23"c)	80~85	80~85	35~55
8	Bending strength	10~15	10~15	16~20
9	tensile strength	6.2	6.2	6~10
10	Soldering resistance temperature (3min)	400"C~480"C	400"C~480"C	400"C~480"C
11	Volume resistance (ohms)	4.7 x10 to the 16th power	4.7 x10 to the 16th power	5.2x10 to the 13th power
12	surface resistance	5.8x10 to the 16th power	5.8x10 to the 16th power	2.5x10 to the 13th power
13	Insulation breakdown voltage (KV/MM)	22	22	18~20
14	Water absorption rate	0.3%	0.3%	0.3%
15	Shelf life	25"C/22 months 5" C/3 months	25"C/22 months 5" C/3 months	25"C/22 months 5" C/3 months

Instructions for use:
1. The workplace should be clean. Air circulation must be installed when necessary.
2. Since the product is a chemical product that reacts when heated, the temperature of the environment has a great influence on the quality of the product. Please keep the product in a low temperature environment to ensure the stability and quality of the product. During use, the product is prone to gelation or a decrease in bond strength.
3. If the gel is not used up after removal, please seal it tightly and put it in a frozen environment.